Influence of CO annealing in metal-oxide-semiconductor capacitors with SiO2 films thermally grown on Si and on SiC

  • Understanding the influence of SiC reaction with CO, a by-product of SiC thermal oxidation, is a key point to elucidate the origin of electrical defects in SiC metal-oxide-semiconductor (MOS) devices. In this work, the effects on electrical, structural, and chemical properties of SiO2/Si and SiO2/SiC structures submitted to CO annealing were investigated. It was observed that long annealing times resulted in the incorporation of carbon from CO in the Si substrate, followed by deterioration of the SiO2/Si interface, and its crystallization as SiC. Besides, this incorporated carbon remained in the Si surface (previous SiO2/Si region) after removal of the silicon dioxide film by HF etching. In the SiC case, an even more defective surface region was observed due to the CO interaction. All MOS capacitors formed using both semiconductor materials presented higher leakage current and generation of positive effective charge after CO annealings. Such results suggest that the negative fixed charge, typically observed in SiO2/SiC structures, isUnderstanding the influence of SiC reaction with CO, a by-product of SiC thermal oxidation, is a key point to elucidate the origin of electrical defects in SiC metal-oxide-semiconductor (MOS) devices. In this work, the effects on electrical, structural, and chemical properties of SiO2/Si and SiO2/SiC structures submitted to CO annealing were investigated. It was observed that long annealing times resulted in the incorporation of carbon from CO in the Si substrate, followed by deterioration of the SiO2/Si interface, and its crystallization as SiC. Besides, this incorporated carbon remained in the Si surface (previous SiO2/Si region) after removal of the silicon dioxide film by HF etching. In the SiC case, an even more defective surface region was observed due to the CO interaction. All MOS capacitors formed using both semiconductor materials presented higher leakage current and generation of positive effective charge after CO annealings. Such results suggest that the negative fixed charge, typically observed in SiO2/SiC structures, is not originated from the interaction of the CO by-product, formed during SiC oxidation, with the SiO2/SiC interfacial region.show moreshow less

Export metadata

Additional Services

Search Google Scholar
Metadaten
Author: E. Pitthan, R. dos Reis, Silma Alberton Corrêa, Dieter SchmeißerORCiD, H. I. Boudinov, F. C. Stedile
DOI:https://doi.org/10.1063/1.4939836
ISSN:0021-8979
ISSN:1089-7550
Title of the source (English):Journal of Applied Physics
Document Type:Scientific journal article peer-reviewed
Language:English
Year of publication:2016
Tag:CO annealing; metal-oxide-semiconductor; silicon; silicon carbide
Issue number:119
First Page:025307-1
Last Page:025307-6
Faculty/Chair:Fakultät 1 MINT - Mathematik, Informatik, Physik, Elektro- und Informationstechnik / FG Angewandte Physik und Halbleiterspektroskopie
Institution name at the time of publication:Fakultät für Mathematik, Naturwissenschaften und Informatik (eBTU) / LS Angewandte Physik / Sensorik
Einverstanden ✔
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.